泡沫温拌再生沥青抗疲劳性能

发布时间:2018-10-08 11:45
【摘要】:为了研究回收沥青掺量对泡沫温拌再生沥青抗疲劳性能的影响,采用三大指标试验、动态剪切流变试验和扫描电镜试验,测试了不同回收沥青掺量下的泡沫温拌再生沥青抗疲劳性能的变化。试验结果表明:随着回收沥青掺量的增加,泡沫温拌再生沥青的疲劳因子和极限疲劳温度值逐渐增大,疲劳寿命值不断减小,抗疲劳性能不断变差;当回收沥青掺量大于等于60%(质量分数)时,泡沫温拌再生沥青的抗疲劳能力显著变差。回收沥青使泡沫温拌再生沥青的表面由光滑细腻逐渐变为清晰的褶皱,刚性增强。
[Abstract]:In order to study the effect of recycled asphalt content on the fatigue resistance of recycled foam asphalt, three index tests, dynamic shear rheological test and scanning electron microscope test were used. The change of fatigue resistance of foam warm-mixed recycled asphalt with different content of recycled asphalt was tested. The experimental results show that the fatigue factor and limit fatigue temperature of the recycled foam asphalt increase gradually with the increase of the amount of recycled asphalt, the fatigue life value decreases and the fatigue resistance performance becomes worse. When the content of recycled asphalt is more than 60% (mass fraction), the fatigue resistance of foam warm mix recycled asphalt becomes worse. The recovered asphalt makes the surface of the foam warm-mixed recycled asphalt gradually change from smooth and fine to clear fold and strengthen the rigidity.
【作者单位】: 云南省交通规划设计研究院;扬州大学水利与能源动力工程学院;
【基金】:江苏省自然科学青年基金项目(BK20160471)
【分类号】:U414

【相似文献】

相关期刊论文 前10条

1 安中华,杨彦海,徐雅峰,孔国永;灰色关联分析法评价再生沥青的性能关系[J];辽宁交通科技;2003年06期

2 王洋;廖克俭;王洪国;陆伟强;;鞍山千山公路再生沥青老化研究[J];化工科技;2012年02期

3 ;江西省公路管理局召开旧路再生沥青养护新技术现场观摩会[J];石油沥青;2013年04期

4 李波;;道路再生沥青与混凝土配比研究[J];内蒙古公路与运输;2014年01期

5 陈义兵;;再生沥青混合料配合比设计技术[J];安徽建筑;2007年05期

6 李进;张玉贞;;工厂热拌再生沥青混凝土技术综述[J];石油沥青;2008年01期

7 丁湛;栗培龙;;再生沥青的黏度复合模型研究[J];新型建筑材料;2008年05期

8 杨秋浩;;再生沥青混凝土质量控制因素研究[J];科技创新导报;2011年12期

9 周彬;连瑞雪;;再生沥青养护法在公路养护中的作用分析[J];科技信息;2012年09期

10 任晨;;温拌再生沥青混凝土性能研究[J];上海公路;2012年04期

相关会议论文 前2条

1 徐f,

本文编号:2256618


资料下载
论文发表

本文链接:https://www.wllwen.com/kejilunwen/daoluqiaoliang/2256618.html


Copyright(c)文论论文网All Rights Reserved | 网站地图 |

版权申明:资料由用户6a27b***提供,本站仅收录摘要或目录,作者需要删除请E-mail邮箱bigeng88@qq.com