硫磺改性乳化沥青的制备及其储存稳定性研究
发布时间:2018-06-21 09:34
本文选题:硫磺 + 改性沥青 ; 参考:《石油炼制与化工》2017年05期
【摘要】:以胜利70号基质沥青为原料,在反应温度为130℃条件下加入10%(w)硫磺,首先制备硫磺改性沥青,然后在乳化剂A添加量为3.0%、增稠剂聚丙烯酰胺添加量为0.45%、稳定剂KCl添加量为1.5%的条件下乳化,制备了硫磺改性乳化沥青。通过针入度、软化点、延度、储存稳定性及恩氏黏度等的测定,研究了乳化剂A和增稠剂添加量、硫磺改性方式及添加量等对改性乳化沥青性能和储存稳定性的影响。评价结果表明,制备的硫磺改性乳化沥青能够满足普通乳化沥青标准的技术要求。
[Abstract]:With Shengli No. 70 matrix asphalt as raw material, 10% (W) sulphur was added at the reaction temperature of 130 C. First, sulfur modified asphalt was prepared, then emulsifier A was added to 3%, thickener polyacrylamide was added 0.45%, and the addition of stabilizer KCl was 1.5%. The sulfur modified emulsified asphalt was prepared by needle penetration and soft. The effects of emulsifier A and thickener addition, sulfur modification method and addition amount on the performance and storage stability of modified emulsified bitumen are studied. The results show that the prepared sulphur modified emulsified bitumen can meet the technical requirements of ordinary emulsified bitumen.
【作者单位】: 华东理工大学大型工业反应器工程教育部工程研究中心;中国石化齐鲁分公司研究院;中国石化洛阳分公司;
【分类号】:U414
【相似文献】
相关期刊论文 前10条
1 王秀平;张祥;李晓林;郑广宇;张立群;;脱硫胶粉改性沥青储存稳定性的研究[J];特种橡胶制品;2013年05期
2 ;来函照登[J];重庆交通大学学报(自然科学版);2012年04期
3 张俊亮;张静;程国香;陈保莲;;提高乳化沥青储存稳定性的方法研究[J];石油沥青;2013年04期
4 谢利宝;杨建新;凌晨;;浅谈乳化沥青的储存稳定性[J];公路交通科技;2006年09期
5 张兰;;水溶性高分子在提高乳化沥青储存稳定性方面的应用[J];公路交通科技(应用技术版);2007年11期
6 黎侃;李洁;刘毅;;改善SBS聚合物改性沥青储存稳定性的措施[J];上海公路;2006年01期
7 林先焰;陈金国;孟令峰;;SBS改性沥青储存稳定性及试验研究[J];山西建筑;2012年04期
8 熊萍,郝培文;SBS改性沥青储存稳定性试验方法和评价指标的研究[J];中国公路学报;2005年01期
9 冯新军;郝培文;;SBS聚合物改性沥青热储存稳定性取样方法和评价指标[J];长沙理工大学学报(自然科学版);2006年02期
10 孙大权;吕伟民;;SBS改性沥青热储存稳定性研究[J];建筑材料学报;2006年06期
,本文编号:2048104
本文链接:https://www.wllwen.com/kejilunwen/daoluqiaoliang/2048104.html