微波辐照法制备PVC-g-DAP聚合物及其结构与性能表征

发布时间：2018-01-23 20:15

  本文关键词： 聚氯乙烯 邻苯二甲酸二烯丙酯 微波辐照 接枝改性 流变性能　出处：《高分子材料科学与工程》2016年08期 　论文类型：期刊论文

【摘要】：采用微波辐照法制备了以聚氯乙烯(PVC)为骨架,邻苯二甲酸二烯丙酯(DAP)为支链的接枝聚合物PVC-g-DAP。通过红外光谱、差示扫描量热分析对聚合物的结构进行了表征,同时对聚合物的流变性能、耐热性和力学性能进行了测试分析。结果表明,DAP在微波辐照下成功接枝到PVC大分子链上,PVC-g-DAP聚合物只有1个Tg,且略高于PVC。PVC-g-DAP聚合物的流变性能较PVC有大幅度改善,同时力学性能、耐热性得到提升。
[Abstract]:The graft polymer PVC-g-DAPs with polyvinyl chloride (PVC) as skeleton and diallyl phthalate (DAPs) as branching chain was prepared by microwave irradiation. The structure of the polymer was characterized by differential scanning calorimetry (DSC), and the rheological properties, heat resistance and mechanical properties of the polymer were tested and analyzed. DAP was successfully grafted onto the macromolecular chain of PVC under microwave irradiation, and the PVC-g-DAP polymer was only 1 TG. The rheological property of the polymer is slightly higher than that of the PVC.PVC-g-DAP polymer, and the mechanical properties and heat resistance of the polymer are greatly improved than that of the PVC polymer.
【作者单位】： 四川大学高分子研究所高分子材料工程国家重点实验室;
【基金】：横向项目(JG2014050)
【分类号】：TQ325.3
【正文快照】： 常规自由基聚合所得的聚氯乙烯(PVC)分子呈线型无规缠绕状态,分子链上含有大量强极性的C-Cl结构,分子间作用力大,导致PVC熔体黏度高,流动性差,加工性能不理想[1,2]。因此,提高PVC树脂的熔体流动性,改善其加工性能一直是PVC工业的研究热点之一。近年来,研究人员提出了多种物理，

本文编号：1458144