冷轧SIMA法制备镁合金半固态坯料的组织与性能

发布时间：2018-08-14 19:18

【摘要】：利用冷轧与半固态热处理工艺(冷轧SIMA法)制备了AZ91D镁合金半固态坯料,研究了不同冷轧压下量对半固态坯料显微组织与压缩性能的影响,并探讨了固相颗粒的球化机制与半固态坯料的成形机制。结果表明:随着冷轧压下量的增加,固相颗粒的平均尺寸逐渐的减小、球形率逐渐地增大,液相率逐渐地增大,而半固态坯料的压缩性能呈先升后降的趋势;当冷轧压下量低于8.72%时,对半固态坯料显微组织的影响较为敏感。半固态加热时,固相颗粒的原子尺度界面由光滑小晶面转变为粗糙非小晶面,宏观表现为多边形转变为球形;且随着冷轧压下量的增大,该球形化过程的转变速度显著提高。
[Abstract]:The semi-solid blank of AZ91D magnesium alloy was prepared by cold rolling and semi-solid heat treatment (SIMA method). The effect of different cold rolling reduction on microstructure and compression properties of semi-solid billet was studied. The spheroidizing mechanism of solid particles and the forming mechanism of semi-solid billets were discussed. The results show that the average size of solid particles decreases gradually, the spherical rate increases gradually and the liquid phase ratio increases with the increase of cold rolling reduction, while the compression performance of semi-solid billets increases first and then decreases. When the reduction of cold rolling is lower than 8.72, the effect of cold rolling on the microstructure of semi-solid billet is more sensitive. When semi-solid is heated, the atom-scale interface of the solid particles changes from smooth microcrystalline plane to rough non-small crystal surface, and the macroscopic appearance is polygon to spherical, and with the increase of cold rolling reduction, the transformation speed of the sphericity process increases remarkably.
【作者单位】： 华北理工大学冶金与能源学院;
【基金】：国家自然科学基金(51474091) 河北省自然科学基金(E2013209268) 华北理工大学大学生创新创业训练计划项目(X2015039)
【分类号】：TG146.22;TG339

【相似文献】

相关期刊论文 前10条

1 闫洪,张发云,揭小平;Structure evolution of AZ61 magnesium alloy in SIMA process[J];Transactions of Nonferrous Metals Society of China;2005年03期

2 ;Effects of compressing and remelting in SIMA processing on semi-solid structure evolution of an Al-Zn wrought alloy[J];Rare Metals;2003年03期

3 薛克敏;弭光宝;王清瑞;;Compound fabrication technology of semi-solid billet of Al-Si alloy based on SIMA method[J];Transactions of Nonferrous Metals Society of China;2006年S3期

4 姜巨福;王迎;曲建俊;杜之明;罗守靖;;Preparation and thixoforging of semisolid billet of AZ80 magnesium alloy[J];Transactions of Nonferrous Metals Society of China;2010年09期

5 王振宇;吉泽升;孙丽鑫;许红雨;;Microstructure of semi-solid ADC12 aluminum alloy adopting new SIMA method[J];Transactions of Nonferrous Metals Society of China;2010年S3期

6 姜巨福;罗守靖;;Preparation of semi-solid billet of magnesium alloy and its thixoforming[J];Transactions of Nonferrous Metals Society of China;2007年01期

7 姜巨福;罗守靖;邹经湘;;Preparation of AZ91D magnesium alloy semi-solid billet by new strain induced melt activated method[J];Transactions of Nonferrous Metals Society of China;2006年05期

8 ;EFFECT OF PREDEFORMATION MANNER ON SEMI-SOLID STRUCTURE OF AZ61 MAGNESIUM ALLOY IN SIMA PROCESS[J];Acta Metallurgica Sinica(English Letters);2008年03期

9 姜巨福;彭秋才;单巍巍;罗守靖;;新SIMA法制备AZ91D半固态坯[J];特种铸造及有色合金;2005年12期

10 祁红璋;李成魁;严彪;蒋凯雁;;A4020铝合金活塞的SIMA法制备及微观组织研究[J];特种铸造及有色合金;2009年09期

相关会议论文 前5条

1 王卫卫;韩飞;;LC9铝合金在SIMA法半固态处理过程中的组织演化[A];第八届全国塑性加工学术年会论文集[C];2002年

2 王卫卫;韩飞;;LC9铝合金在SIMA法半固态处理过程中的组织演化[A];第二届半固态金属加工技术研讨会论文集[C];2002年

3 王卫卫;韩飞;;LC9铝合金在SIMA法半固态处理过程中的组织演化[A];第八届全国塑性加工学术年会论文集[C];2002年

4 李元东;郝远;阎峰云;;SIMA法对AZ91D镁合金非枝晶组织的细化作用[A];第八届全国塑性加工学术年会论文集[C];2002年

5 李元东;郝远;阎峰云;;SIMA法对AZ91D镁合金非枝晶组织的细化作用[A];第二届半固态金属加工技术研讨会论文集[C];2002年

相关硕士学位论文 前5条

1 弭光宝;基于SIMA法的近共晶点铝硅合金半固态坯料复合制备研究[D];合肥工业大学;2007年

2 韩国民;基于新SIMA法的AlSi30合金半固态坯料制备试验研究[D];合肥工业大学;2009年

3 董传勇;基于SIMA法的AlSi30合金半固态坯料复合制备技术研究[D];合肥工业大学;2010年

4 夏明许;SIMA法制备半固态镁合金的研究[D];西安理工大学;2003年

5 姚亮宇;SIMA法压缩形变镁合金半固态组织的研究[D];西安理工大学;2004年

，

本文编号：2183864