热致发泡法制备高密度聚乙烯微泡塑料研究

发布时间：2019-06-22 14:30

【摘要】：利用单螺杆挤出机将高密度聚乙烯(HDPE)和发泡剂H(二亚硝基五次甲基四胺)进行反应挤出热发泡,制备出了精细泡孔结构的微泡塑料。研究了挤出温度、螺杆转速、发泡剂H用量对挤出产物泡孔结构的影响。结果表明:随着挤出温度、螺杆转速、发泡剂H用量的增加,挤出产物的泡孔平均直径降低,泡孔密度增大。当发泡剂H质量分数14%时,HDPE微泡塑料的泡孔平均直径达到65μm。
[Abstract]:Microfoam with fine bubble structure was prepared by reactive extrusion of high density polyethylene (HDPE) and foaming agent H (dinitronitro pentmethylenetetramine) by single screw extruder. The effects of extrusion temperature, screw speed and foaming agent H content on the bubble structure of extrusion products were studied. The results show that with the increase of extrusion temperature, screw speed and the dosage of foaming agent H, the average diameter of foam decreases and the density of foam increases with the increase of extrusion temperature, screw speed and foaming agent H content. When the mass fraction of foaming agent H is 14%, the average diameter of foam pores of HDPE microfoam plastics reaches 65 渭 m.
【作者单位】： 大连理工大学化工学院高分子材料系;
【分类号】：TQ328

【相似文献】

相关期刊论文 前10条

1 余作兴,赵德仁;高分子微泡的研究——Ⅰ.二烯丙基二(十二烷基)季铵盐的合成与聚合[J];功能高分子学报;1988年01期

2 周荣才,梁玉增,陈志良,管爱国,赵德仁;高分子微泡体系中光解水的研究——(Ⅱ)聚卵磷脂微泡在光解水中的应用[J];功能高分子学报;1990年02期

3 王朋娇;对微泡片制片新法的质疑[J];感光材料;1999年06期

4 肖欢;杨春江;唐毅;王荞;王冬;高洋;陈镜宇;高惠;王莹;;载氧脂质微泡体外释氧效果[J];中国介入影像与治疗学;2013年08期

5 戴葆青;李伟;吴延娜;;微泡发生器的数值模拟分析[J];煤矿机械;2012年12期

6 冯敏;赵洪洋;张丽;刘莹莹;谢明星;符荣;;纳米级脂质微泡的制备及其在动脉血栓检测中的应用[J];临床心血管病杂志;2009年12期

7 唐侔;微泡辊涂技术[J];西部皮革;1994年03期

8 魏亚飞;杨晓京;谢军;;一种新型微泡发生器的流场仿真研究[J];机械研究与应用;2008年05期

9 宗瑜瑾;万明习;王素品;;包膜超声造影微泡的计算机辅助设计、制备与实验研究[J];航天医学与医学工程;2006年01期

10 朱斌;许时婴;夏书芹;;脂质体空气微泡的制备[J];食品与生物技术学报;2007年03期

相关会议论文 前10条

1 柳建华;萧淑宜;何景光;区文财;邱春花;冯桂英;;微泡联合低强度治疗超声对犬睾丸组织及细胞影响的研究[A];中国超声医学工程学会第九届全国腹部超声医学学术会议论文汇编[C];2012年

2 张群霞;王志刚;冉海涛;李晓东;郑元义;景香香;;不同超声强度及微泡对基因和组织作用的实验研究[A];第九届全国超声医学学术会议论文汇编[C];2006年

3 姜学平;程茜;钱梦，

本文编号：2504670