一步法制备钒铝合金的影响因素探究

发布时间：2018-01-22 13:52

  本文关键词： 钒铝合金 一步法 投料模式 原料品位　出处：《钛工业进展》2017年05期 　论文类型：期刊论文

【摘要】：为提高一步法生产钒铝合金的回收率,研究了投料方式、杂质种类及含量、原料品位等对铝热反应过程及产品化学成分和回收率的影响。结果表明,投料时采用先密实处理再投料的模式,能够使反应原料之间紧密接触,密实程度均匀,产品损耗少;采用Fe、Si含量低的原料,能够减少喷溅现象,降低产品损耗;采用品位高的V2O5,能够加快反应速度,防止发生喷溅,且产品的杂质元素含量较低。
[Abstract]:In order to improve the recovery rate of vanadium aluminum alloy produced by one-step method, the effects of feeding mode, impurity type and content, raw material grade on the process of thermo reaction, chemical composition and recovery rate of the product were studied. The mode of first compacting treatment and then feeding can make the reaction material contact closely, the compactness degree is even, and the product loss is less. The use of low Fesi Si content of raw materials can reduce the spatter phenomenon and reduce the loss of products. High grade V _ 2O _ 5 can accelerate the reaction speed, prevent spatter, and the content of impurity elements in the product is low.
【作者单位】： 宝钛特种金属有限公司;
【分类号】：TF841.3
【正文快照】： 0引言钛及钛合金因密度小、耐腐蚀、比强度高,广泛应用于航空航天、能源、化工、体育、医疗等领域[1]。钒铝中间合金是生产钛合金的重要添加剂,常用的钒铝合金有Al V55、Al V65、Al V85。Al V55作为Ti-6Al-4V合金的主要添加剂,其生产方法主要有一步法(铝热法)和两步法(铝热法+，

本文编号：1454845