液态成型法制备铝基碳化硼中子吸收材料关键技术研究

发布时间：2018-01-24 05:44

  本文关键词： 乏燃料贮存格架 中子吸收材料 液态成型法　出处：《核动力工程》2016年06期 　论文类型：期刊论文

【摘要】：通过对粉体进行表面处理、熔体改性、搅拌分散以及变形控制等工艺,采用液态成型法成功制备出B4C含量为31wt.%的板材。综合分析表明,B4C颗粒弥散均匀地分布在铝基体中,颗粒在轧制过程中未发生择优取向的分布,同时与铝基体保持紧密的界面链接。10B面密度平均为0.0372 g/cm2并保持均匀分布。模拟乏燃料水池介质8000 h的高温加速腐蚀试验结果表明:板材的腐蚀增重变化小于0.5%,辐照对其物理和机械等各项性能的影响有限。
[Abstract]:Through surface treatment, melt modification, agitation dispersion and deformation control, the plate with B _ 4C content of 31wt.% was successfully prepared by liquid forming method. B4C particles distributed uniformly in aluminum matrix, and no preferred orientation occurred during rolling. At the same time, the density of interface. 10B is 0.0372 g / cm ~ 2 and keeps a uniform distribution. Simulation of spent fuel Tank medium 8000. H high temperature accelerated corrosion test results show that the change of corrosion weight gain of sheet metal is less than 0.5%. The effects of irradiation on physical and mechanical properties are limited.
【作者单位】： 中广核工程有限公司;清华大学深圳研究生院;
【分类号】：TL34
【正文快照】： 0引言目前国内乏燃料贮存格架已实现自主化设计,但关键的中子吸收材料仍然主要依靠进口,大大制约了乏燃料贮存格架的国产化进程。因此,加快乏燃料贮存用中子吸收材料的研发和生产工作已刻不容缓。B4C含量以及在基体中是否弥散分布是铝基B4C复合材料能否获得优良中子吸收性能的

【相似文献】

相关期刊论文 前4条

1 李刚;简敏;王美玲;王贯春;刘晓珍;;反应堆乏燃料贮运用中子吸收材料的研究进展[J];材料导报;2011年13期

2 王傲松;李学军;谭经耀;;Al-B_4C中子吸收材料鉴定方法研究[J];金属功能材料;2014年01期

3 王美玲;李刚;陈乐;刘晓珍;孙长龙;刘云明;刘超红;;B_4C-Al中子吸收材料拉伸性能及断裂机理[J];原子能科学技术;2014年05期

4 ;[J];;年期

相关会议论文 前2条

1 李刚;王美玲;付道贵;;B_4C/Al中子吸收材料的力学性能及微观组织研究[A];中国核科学技术进展报告（第二卷）——中国核学会2011年学术年会论文集第4册（核材料分卷、同位素分离分卷、核化学与放射化学分卷）[C];2011年

2 王日中;胡毅;唐可超;;核反应堆用碳化硼材料研究进展[A];中国核科学技术进展报告（第二卷）——中国核学会2011年学术年会论文集第4册（核材料分卷、同位素分离分卷、核化学与放射化学分卷）[C];2011年

相关博士学位论文 前1条

1 张鹏;高含量铝基碳化硼中子吸收材料的制备及性能研究[D];太原理工大学;2014年

，

本文编号：1459311