EIGA法制备激光3D打印用TA15钛合金粉末

发布时间：2018-02-24 13:36

  本文关键词： EIGA法 TA钛合金粉末 激光D打印 粉末可打印性　出处：《材料导报》2017年12期 　论文类型：期刊论文

【摘要】：采用电极感应熔炼气雾化(EIGA)法制备了激光3D打印用TA15钛合金粉末,研究了熔炼功率对粉末收得率、粒径分布、粉末形貌、松装密度和流动性等特征的影响。结果表明,随着感应熔炼功率增大,粉末收得率和平均粒径减小,当熔炼功率为65kW时,粉末收得率超过62%,中值粒径D_(50)小于100μm,松装密度为2.731g/cm3,流动性为22.46s/50g。对粒径50~180μm的粉末采用激光3D打印,激光直接沉积成形的TA15钛合金样品表面无宏观裂纹和气孔等缺陷,金相组织为细晶网篮组织,制备的TA15钛合金粉末具有良好的可打印性。
[Abstract]:TA15 titanium alloy powder for laser 3D printing was prepared by electrode induction melting gas atomization method. The effects of melting power on the recovery rate, particle size distribution, powder morphology, bulk density and fluidity were studied. With the increase of induction melting power, the powder yield and average particle size decrease. When the melting power is 65kW, the powder yield exceeds 62um, the median particle size is less than 100 渭 m, the loose density is 2.731 g / cm ~ 3, and the fluidity is 22.46 s / 50 g. Laser 3D printing is used for the powder with a diameter of 50180 渭 m. There are no macroscopic cracks and pores on the surface of TA15 titanium alloy prepared by laser direct deposition. The microstructure of TA15 titanium alloy powder is fine crystal basket structure. The prepared TA15 titanium alloy powder has good printability.
【作者单位】： 东北大学材料科学与工程学院材料各向异性与织构教育部重点实验室;东北大学鞍山激光应用技术研究院;
【基金】：国家重点研发计划项目(2016YFB1100201) 辽宁省科技计划项目(2014221006) 教育部基本科研业务费重大创新项目(N130810002) 广东省科技计划项目(2015B010122001)
【分类号】：TF123.23

【相似文献】

相关期刊论文 前10条

1 孙洪志;;生产“干净”钛合金粉末的新方法[J];稀有金属合金加工;1980年02期

2 庞美珠;;等离子旋转电极法制取清洁钛合金粉末[J];上海有色金属;1980年06期

3 R.Sundaresan,王世杰;旋转棒法生产钛合金粉末[J];稀有金属材料与工程;1983年06期

4 胡初潜;钛合金粉的快速动态固结[J];稀有金属;1993年03期

5 曾立英;高温下钛合金粉末件的压实性研究[J];稀有金属快报;2002年09期

6 F.H.Froes ,D.Eylon ,廖际常;钛合金粉末冶金[J];稀有金属材料与工程;1986年06期

7 周洪强;陈志强;;钛及钛合金粉末的制备现状[J];稀有金属快报;2005年12期

8 刘学晖,徐广;惰性气体雾化法制取钛和钛合金粉末[J];粉末冶金工业;2000年03期

9 杰拉尔德·弗里德曼 ,屈翠芬;钛粉末冶金[J];稀有金属合金加工;1975年11期

10 王琪;李圣刚;吕宏军;石刚;黄思原;史金靓;;雾化法制备高品质钛合金粉末技术研究[J];钛工业进展;2010年05期

，

本文编号：1530429