基于微波膨胀法制备石墨蠕虫的工艺

发布时间：2018-02-24 20:28

  本文关键词： 石墨蠕虫 微波膨胀 高温加热　出处：《材料科学与工程学报》2017年03期 　论文类型：期刊论文

【摘要】：制备品质优良的石墨蠕虫是石墨烯工业化的研究热点。采用微波膨胀法对可膨胀石墨进行剥离,成功制备得到石墨蠕虫。比较了高温加热法、普通微波设备法、专用微波设备法这三种方法制备石墨蠕虫的效果,结果表明,专用微波设备法制备的石墨蠕虫品质最好,1g可膨胀石墨制备的石墨蠕虫体积可达333mL,比表面积可达280m~2/g。与高温加热法相比,微波膨胀法具有制备速度快、蠕虫品质好、过程节能等优点,是一种大批量生产石墨蠕虫切实可行的方案。
[Abstract]:The preparation of graphite worm with excellent quality is a research hotspot in graphene industry. The graphite worm is prepared successfully by stripping expandable graphite by microwave expansion. The method of high temperature heating and ordinary microwave equipment are compared. The effect of these three methods on the preparation of graphite worms by special microwave equipment method shows that, The quality of graphite worm prepared by special microwave equipment method is the best. The volume of graphite worm prepared by 1g expandable graphite can reach 333mL, and the specific surface area can reach 280mg / g. Compared with high-temperature heating method, microwave expansion method has the advantages of faster preparation speed and better worm quality. Process energy saving is a feasible scheme for mass production of graphite worms.
【作者单位】： 青岛理工大学琴岛学院;
【分类号】：TQ127.11

【相似文献】

相关期刊论文 前6条

1 云中客;;石墨强度的高与低[J];物理;2011年03期

2 侯跃新;肖丹;李岩;李钢;马永和;;石墨片厚度在线检测[J];核电子学与探测技术;2011年12期

3 黄桥;孙红娟;杨勇辉;;氧化石墨的谱学表征及分析[J];无机化学学报;2011年09期

4 张淑娟;M301碳塑复合石墨片等通过函审鉴定[J];碳素;1990年01期

5 曾奇,翟启杰;稀土-氮复合孕育剂对灰铸铁石墨组织的影响[J];中国稀土学报;1997年01期

6 ;[J];;年期

相关硕士学位论文 前2条

1 方小强;纳米石墨片复合膜的制备及其导热性能研究[D];哈尔滨工业大学;2016年

2 房海秋;石墨烯基材料在染料敏化太阳能电池中的应用[D];大连理工大学;2014年

，

本文编号：1531605