外加入法制备高强高导Cu-5wt%Cr复合材料组织性能研究
本文关键词： Cu-Cr复合材料 外加入法 强度 导电性能 纤维组织 出处：《热加工工艺》2016年10期 论文类型：期刊论文
【摘要】：通过采用外加入Cr颗粒方制备Cu-5wt%Cr复合材料,研究了冷拔变形量和中间退火工艺对Cu-5wt%Cr复合材料中纤维组织形成过程及力学性能和导电性的影响。结果表明:随变形量的增加,Cr颗粒变形不均匀;退火使纤维发生弯曲、粗化、溶断等现象;材料的冷拔变形量与合理的中间退火工艺相组合,可得到强度和导电率的良好配合。
[Abstract]:Cu-5wt%Cr composites were prepared by adding Cr particles outside. The effects of cold drawing deformation and intermediate annealing process on the microstructure, mechanical properties and electrical conductivity of fiber in Cu-5wt%Cr composites were studied. The results showed that the deformation of Cr particles was not uniform with the increase of deformation, and the fiber was bent and coarsened by annealing. The combination of cold drawing deformation and reasonable intermediate annealing process can get good coordination of strength and conductivity.
【作者单位】： 河北科技大学材料科学与工程学院;石家庄经济学院;
【分类号】：TB331
【相似文献】
相关期刊论文 前10条
1 毕莉明;刘平;陈小红;刘新宽;李伟;马凤仓;;冷轧Cu-15Cr原位复合材料性能及Cr纤维相高温稳定性[J];中国有色金属学报;2012年04期
2 毕莉明;刘平;陈小红;宋鑫;刘新宽;李伟;马凤仓;;Zr对Cu-15Cr原位复合材料Cr纤维相及性能的影响[J];材料热处理学报;2012年12期
3 ;Cr_(17) Ni_2钢平面应变断裂韧性K_(1c)的测试[J];工学学报;1977年01期
4 黄扬风;曾春林;温靖;;碳纳米管对Cr~(3+)吸附性能的影响[J];广州化工;2010年08期
5 罗骥;方哲成;郭志猛;邵慧萍;;含V和Cr纳米W粉碳化热力学分析及实验[J];材料热处理学报;2011年02期
6 王改莲,吴翠微,董建新,谢锡善;IN718(GH169)合金中α-Cr析出相的研究进展[J];材料工程;2001年06期
7 王改莲,吴翠微,张麦仓,董建新,谢锡善;α-Cr在Incone1718合金中析出行为的微观分析[J];稀有金属材料与工程;2002年01期
8 郑亮,谷臣清,张国庆;Ta对低Cr高W铸造镍基高温合金显微组织的影响[J];稀有金属材料与工程;2005年02期
9 石松耀,徐庆镇,黄钢祥,杨国斌;Cr和Mo对Fe-Si-B非晶磁性和热稳定性的影响[J];上海钢研;1987年04期
10 林金谷，魏狱年，邹炳锁，汪力，王sゾ眨趸ぃ锟耍潞欤夥
本文编号：1537400
本文链接：https://www.wllwen.com/shekelunwen/minzhuminquanlunwen/1537400.html