EDTA对溶胶-凝胶法制备Z型铁氧体的影响

发布时间：2018-03-23 00:11

  本文选题：Z型铁氧体　切入点：溶胶-凝胶法　出处：《兵器材料科学与工程》2016年03期 　论文类型：期刊论文

【摘要】：以EDTA与柠檬酸作为联合络合剂,采用溶胶-凝胶燃烧法制备纯相Z型铁氧体,通过与柠檬酸为络合剂时制备的产物对比,探究EDTA对Z型铁氧体的影响。研究发现,采用两种络合剂制备出的Z型铁氧体,纯度高、磁性能好,在2GHz处的磁导率实部为2.5,同时使Z型铁氧体形成的温度区间变宽,但EDTA的加入只能使Z型铁氧体的烧成温度略微提高。
[Abstract]:Using EDTA and citric acid as the combined complexing agent, pure Z-type ferrite was prepared by sol-gel combustion method. The effect of EDTA on Z-type ferrite was studied by comparing the product prepared with citric acid as the complex agent. The Z type ferrite prepared by two kinds of complexing agents has high purity and good magnetic properties. The real part of the permeability at 2GHz is 2.5, and the temperature range of the formation of Z type ferrite is widened at the same time. However, the addition of EDTA can only slightly increase the firing temperature of Z ferrite.
【作者单位】： 山东非金属材料研究所;吉林大学化学学院;
【分类号】：TM277

【相似文献】

相关期刊论文 前10条

1 杨强;黄剑锋;曹丽云;吴建鹏;熊娜;;莫来石微晶的溶胶-凝胶法制备及其表征[J];人工晶体学报;2010年S1期

2 杨明婷;刘连利;孙彤;徐姝颖;孙志佳;吕红艳;;溶胶-凝胶法制备硅凝胶块及其防开裂研究[J];渤海大学学报(自然科学版);2012年03期

3 雷芳;徐崇福;杨敏丽;房俊卓;陈昊萍;;溶胶-凝胶法合成蓝色荧光粉SrAl_2Si_2O_8:Eu~(2+)[J];发光学报;2006年04期

4 杨强;黄剑锋;杨婷;曹丽云;吴建鹏;;络合溶胶-凝胶法制备不同形貌的莫来石微晶[J];人工晶体学报;2011年03期

5 俞波,陈一匡,方向明,石旺舟;玻璃表面增透膜的溶胶-凝胶法制备[J];汕头大学学报(自然科学版);2002年02期

6 梁达文,白守礼,杨东,陈霭t，

本文编号：1651021