利用高铝粉煤灰种分法制备拟薄水铝石的基础研究

发布时间：2018-04-05 02:22

  本文选题：高铝粉煤灰　切入点：晶种分解　出处：《有色金属(冶炼部分)》2016年08期

【摘要】：以高铝粉煤灰熟料经预脱硅—碱石灰烧结、溶出、二次脱硅后溶液为原料,通过晶种分解后生产拟薄水铝石产品,考察了种分条件对拟薄水铝石产品的影响,并对其进行表征。结果表明,种分法制备的拟薄水铝石产品孔容可达到0.829 1cm3/g,BET比表面积高达393.00m2/g,达到并优于普通大孔拟薄水铝石的理化指标,从而可实现高铝粉煤灰中铝资源的高附加值利用。
[Abstract]:The pseudo-boehmite product was produced from high-alumina fly ash clinker by pre-desilication alkali lime sintering dissolution and secondary desilication as raw material. The effect of seed separation conditions on pseudo-boehmite product was investigated and characterized.The results show that the pore volume of pseudo-boehmite prepared by seed separation method can reach 0.829 cm ~ (3) / g ~ (-1) BET specific surface area up to 393.00 m ~ (2 / g), which reaches and is superior to the physical and chemical index of ordinary large pore pseudo-boehmite, thus realizing the high added value utilization of aluminum resources in high-alumina fly ash.
【作者单位】： 东北大学多金属共生矿生态化利用教育部重点实验室;
【基金】：国家自然科学基金资助项目(U1202274) 中央高校基本科研业务费专项资金项目(N140203005,N140204015) 中国博士后科学基金项目(2015M581352)
【分类号】：TF821;TQ536.4

【相似文献】

相关期刊论文 前6条

1 曾双亲;杨清河;肖成武;余波;;干燥方式及老化条件对拟薄水铝石性质的影响[J];石油炼制与化工;2012年06期

2 赵传鸿;拟薄水铝石胶溶性能的研究及打浆贮存应用[J];齐鲁石油化工;2005年04期

3 张孔远;韩红亮;周然然;燕京;;磷改性拟薄水铝石性能及在蜡油加氢催化剂中的应用[J];工业催化;2010年02期

4 李雪礼;娄来银;谭争国;张海涛;段宏昌;李荻;潘志爽;高雄厚;;拟薄水铝石的性质及其在催化裂化催化剂中的应用[J];石化技术与应用;2014年01期

5 申明乐;;利用PS铝基材版酸洗碱洗处理废液制备拟薄水铝石[J];环境工程学报;2010年11期

6 ;[J];;年期

相关硕士学位论文 前1条

1 徐登清;大孔拟薄水铝石制备及加氢脱氧的研究[D];曲阜师范大学;2011年

，

本文编号：1712775