固相反应法制备镝铕共掺硅酸盐荧光粉材料及其应用研究

发布时间：2018-06-22 19:41

  本文选题：CaMgSiO∶Eu + Dy　； 参考：《粉末冶金工业》2017年06期

【摘要】：采用固相反应法制备了镝铕共掺硅酸盐(Ca_2MgSi_2O_7∶Eu,Dy)长余辉荧光粉材料,并制备成荧光涂料,研究其应用特性。通过X射线衍射、荧光光谱、余辉衰减对材料的晶型及发光特性进行了研究。结果表明,荧光粉的晶体结构没有随着稀土离子的掺入而发生变化,在382 nm处荧光粉存在最强激发峰,发射光谱最强发射峰为531 nm,余辉时间长达15 h。随着涂料中荧光粉掺入浓度的提高,涂料涂层的荧光强度、黏度和固化后硬度明显增强,吸水率显著下降。基于Ca_2MgSi_2O_7∶Eu,Dy材料所制备的荧光涂料具有余辉时间长、耐候性优等特点,在荧光涂料领域具有一定的应用潜力。
[Abstract]:The long afterglow phosphors of dysprosium europium co-doped silicate (Ca2MgSiS _ 2O _ 7: EU _ (Dy) were prepared by solid state reaction. The fluorescent coatings were prepared and their application characteristics were studied. The crystal structure and luminescence characteristics of the materials were studied by X-ray diffraction, fluorescence spectra and afterglow decay. The results show that the crystal structure of the phosphors does not change with the doping of rare earth ions. There is the strongest excitation peak at 382 nm, the strongest emission peak is 531 nm, and the afterglow time is 15 h. With the increase of the concentration of phosphor in the coating, the fluorescence intensity, viscosity and hardness of the coating increased obviously, and the water absorption decreased significantly. The fluorescent coatings based on Ca2MgSi2O7: EuDy have long afterglow time, excellent weathering resistance, and have a certain application potential in the field of fluorescent coatings.
【作者单位】： 阿拉善职业技术学院化工系;
【基金】：内蒙古自治区高等学校科学研究项目(NJZC16548)
【分类号】：TQ422

【相似文献】

相关期刊论文 前1条

1 吐尔逊·阿不都热依木,张校刚;溶剂对固相反应法制备H_7PW_(12)O_(42)掺杂聚苯胺的影响[J];功能高分子学报;2003年04期

相关博士学位论文 前1条

1 宋涛;基于主客体系金属—有机框架材料的光谱调控及其白光发射性能研究[D];浙江大学;2017年

相关硕士学位论文 前5条

1 关安翔;单一基质光色可调白光荧光粉的合成及其光学性质研究[D];广西大学;2017年

2 江建青;(Ca_(1-x)M_x)_2SiO_4:Ce~(3+),Al~(3+)(M=Mg,Sr,Ba)荧光粉的制备与发光性能研究[D];江西理工大学;2017年

3 高勇;Eu~(3+)掺杂磷酸盐和钼酸盐的制备及阳离子对发光性能影响的研究[D];广西大学;2017年

4 李美玉;铈离子掺杂钇铝石榴石荧光材料的制备、结构及其光学性能研究[D];广西大学;2017年

5 张波;稀土掺杂钒酸盐的控制合成及发光性能研究[D];安徽建筑大学;2017年

，

本文编号：2054018