真空碳热法制备金属镁过程中可逆反应对镁蒸气冷凝的影响

发布时间：2018-07-05 20:46

本文选题：真空 + 冷凝温度　；参考：《真空科学与技术学报》2016年07期

【摘要】：对真空碳热法制备金属Mg过程中可能发生的逆反应进行了热力学分析,结果表明,系统压力为60 Pa,且温度低于900 K的条件下,冷凝过程中会有逆反应发生。实验研究表明,冷凝温度越接近镁的露点温度,直收率越高。通过对还原产物和蒸馏产物的X射线衍射、扫描电镜及X射线光电子能谱仪的对比分析可以发现,还原产物在受到逆反应的影响的条件下,所形成的镁粉晶粒排列不规则且尺寸较小:而没有逆反应影响所形成的金属Mg晶粒排列规则致密且尺寸较大,因此有效控制逆反应的发生成为收集到结晶较好金属Mg的关键。
[Abstract]:The thermodynamics analysis of the possible inversion during the preparation of metal mg by vacuum carbothermal method is carried out. The results show that the inverse reaction will occur in the condensation process under the pressure of 60 Paand the temperature below 900K. The experimental results show that the closer the condensation temperature is to the dew point temperature of magnesium, the higher the direct yield is. The results of X-ray diffraction, scanning electron microscopy and X-ray photoelectron spectroscopy show that the reduction products are affected by inverse reaction. The resulting magnesium powders have irregular grain arrangement and smaller size: the resulting mg grains are regular dense and larger in size without the influence of inverse reaction. Therefore, controlling the occurrence of inverse reaction effectively becomes the key to the collection of mg with better crystallization.
【作者单位】：复杂有色金属资源清洁利用国家重点实验室;昆明理工大学真空冶金国家工程实验室;云南省有色金属真空冶金重点实验室;云南省复杂有色金属资源清洁利用协同创新中心;
【基金】：国家自然科学青年基金项目(NO.51304095) 云南省复杂有色金属资源综合利用协同创新自设基金项目(NO.2014XTZS005) 教育部“创新团队发展计划”(IRT1250) 有色金属真空冶金科技部重点领域创新团队(NO.2014RA4018)
【分类号】：TF822

【相似文献】