PVD法制备6.5%Si高硅钢过程合金磁性能演化机理研究

发布时间：2018-10-31 07:50

【摘要】：PVD法制备Fe-6.5%Si(质量分数,下同)高硅钢过程基片预处理工艺以及Si渗入对合金的软磁性能均有显著影响。采用磁损耗分离的方法剖析铁硅合金磁性变化的内在机理。采用四探针方法测试合金的电阻率;采用基于热分析仪(DSC)配置永磁场技术测量热重(TG)曲线确定合金的居里温度;采用振动样品磁强计(VSM)测定了材料的饱和质量磁矩;采用直流测试装置和硅钢测试仪测试合金的直流交流软磁性能。PVD法制备6.5%Si高硅钢最大磁导率达到16 400,相比于初始态3%低硅钢基片,铁损值降低40%~50%。
[Abstract]:The preparation of Fe-6.5%Si (mass fraction) by PVD method and the pretreatment process of high silicon steel substrate as well as the infiltration of Si have significant effects on the soft magnetic properties of the alloy. The internal mechanism of magnetic change of Fe-Si alloy was analyzed by magnetic loss separation method. The resistivity of the alloy was measured by four-probe method, and the Curie temperature of the alloy was determined by the thermogravimetric (TG) curve based on the (DSC) configuration of the thermal analyzer. The saturation mass magnetic moment of the material was measured by vibrating sample magnetometer (VSM). The DC soft magnetic properties of the alloy were measured by DC test device and silicon steel tester. The maximum permeability of 6.5%Si high silicon steel prepared by PVD method is 16 400, which is 40% lower than that of the initial 3% low silicon steel substrate.
【作者单位】： 兰州交通大学国家绿色镀膜工程中心;开封大学机械与汽车工程学院;北京航空航天大学材料科学与工程学院;
【基金】：国家自然科学基金资助项目(51461028) 国家科技支撑计划资助项目(2014BAF01B01)
【分类号】：TM275

【相似文献】

相关期刊论文 前2条

1 林均品;叶丰;陈国良;王艳丽;梁永锋;金吉男;刘艳;;6.5wt%Si高硅钢冷轧薄板制备工艺、结构和性能[J];前沿科学;2007年02期

2 ;[J];;年期

相关重要报纸文章 前1条

1 王晖余;要具备独当一面的能力[N];人民日报海外版;2008年

相关博士学位论文 前3条

1 秦镜;轧制法制备低铁损高磁感高硅钢及其涂层研究[D];北京科技大学;2016年

2 李晓;EB-PVD制备高硅钢箔及后处理工艺研究[D];哈尔滨工业大学;2008年

3 杨海丽;熔盐脉冲电沉积制备高硅钢的研究[D];燕山大学;2011年

相关硕士学位论文 前6条

1 刘注显;高硅钢薄板形变与再结晶织构演变研究[D];东北大学;2010年

2 张瑞琦;取向高硅钢薄带冷轧和退火过程中的组织及结构演变[D];东北大学;2014年

3 王旭;CVD法制备高硅钢的工艺过程研究[D];华东理工大学;2013年

4 魏鼎;合金元素对6.5%wtSi高硅钢组织及塑性的影响[D];武汉科技大学;2010年

5 李慧;熔盐电沉积法制备无取向Fe-6.5wt%Si薄板的研究[D];河北理工大学;2009年

6 何朋非;Ti对含硅钢Fe-Zn反应的抑制作用及Zn-Fe-Si-Ti体系相关系的研究[D];湘潭大学;2012年

，

本文编号：2301437