氮化铝真空氯化歧化法制备金属铝

发布时间：2018-01-17 12:35

本文关键词：氮化铝真空氯化歧化法制备金属铝　出处：《真空科学与技术学报》2016年08期 　论文类型：期刊论文

【摘要】：采用热力学计算和动力学模拟以及X射线衍射,扫描电镜的检测手段,对Al N真空条件下的氯化歧化反应进行了研究。热力学计算结果表明:系统压力在10~100 Pa时,Al N的氯化反应起始温度为1428 K,并且冷凝温度必须降低到1064 K以下,才能分解出金属Al;动力学模拟表明:Al Cl3分子与Al N有较强的化学吸附,易发生反应;实验结果表明:温度越高,原料的失重率和金属Al的直收率越大,保温时间延长,也有利于反应的充分进行。实验最终可以制得20~300μm,纯度达99.28%以上球形度完好的铝珠。
[Abstract]:Thermodynamic calculation, kinetic simulation, X-ray diffraction and scanning electron microscopy were used. The chlorination reaction of Al N in vacuum was studied. The thermodynamic calculation results showed that the starting temperature of chlorination reaction of Al N was 1428 K when the pressure of the system was 10 ~ 100 Pa. And the condensation temperature must be reduced to below 1064K in order to decompose metal Al; The kinetic simulation shows that the chemical adsorption of Al _ (Cl3) molecule to Al _ N is strong and the reaction is easy to occur. The experimental results show that the higher the temperature, the greater the weight loss rate of raw material and the higher the direct yield of Al, and the longer the holding time, the more favorable the reaction is. Aluminum beads with purity of more than 99.28% sphericity.
【作者单位】：昆明理工大学真空冶金国家工程实验室;云南省有色金属真空冶金重点实验室;省部共建复杂有色金属资源清洁利用国家重点实验室;云南冶金集团股份有限公司;
【基金】：昆明理工大学生创新创业训练计划(201410674262) 云南省科持领军人才培养计划(2014HA003) 国家自然科学基金地区基金(51264023)
【分类号】：TF821
【正文快照】： 铝是一种高强度的能量载体,在电池、合金、电缆等许多方面有良好的使用性能。铝制品在国民经济多个领域的广泛应用,使得各行业对铝的需求量逐年增加,从而铝的供应数量也随之增大。目前,工业上生产金属Al的方法是电解铝法,而此方法存在着工艺能耗大,过程中会产生氟化物、SO2等