离心转子法制备纳米纤维技术研究
发布时间：2018-08-29 13:19
【摘要】：介绍了几种常见的纳米纤维制备方法,并对他们进行了比较分析。提出一种改进型离心转子制备纳米纤维装置,该装置具有可连续供料、收集距离可调、可适应纺丝盘或针筒等特点。分析了离心转子法制备纳米纤维的工作原理,并对纳米纤维制备过程中喷丝头处的聚合物射流进行运动分析。运用三维设计平台SolidWorks进行了离心转子纳米纤维制备装置的三维设计、装配与仿真,以及所有零件加工图的绘制,进行了装置的试制与装配调试,构建了基本的实验平台,并进行了初步纳米纺丝实验。
[Abstract]:This paper introduces several common preparation methods of nanofibers and makes a comparative analysis of them.An improved centrifugal rotor device for preparing nanofibers is proposed.The device has the characteristics of continuous feeding,adjustable collection distance and adaptability to spinning disk or needle barrel.The working principle of preparing nanofibers by centrifugal rotor method is analyzed. In the process of fiber preparation, the polymer jet at the spinneret head was analyzed. The three-dimensional design platform SolidWorks was used to design, assemble and simulate the centrifugal rotor nanofiber preparation device, and draw the processing drawings of all parts. The preliminary nanoscale spinning experiments were carried out.
【作者单位】： 武汉纺织大学机械工程与自动化学院;湖北数字化纺织装备重点实验室;迪肯大学前沿材料学院;
【基金】：湖北省科技支撑计划对外科技合作类项目(2014BHE010)
【分类号】：TB383.1;TQ340.6
[Abstract]:This paper introduces several common preparation methods of nanofibers and makes a comparative analysis of them.An improved centrifugal rotor device for preparing nanofibers is proposed.The device has the characteristics of continuous feeding,adjustable collection distance and adaptability to spinning disk or needle barrel.The working principle of preparing nanofibers by centrifugal rotor method is analyzed. In the process of fiber preparation, the polymer jet at the spinneret head was analyzed. The three-dimensional design platform SolidWorks was used to design, assemble and simulate the centrifugal rotor nanofiber preparation device, and draw the processing drawings of all parts. The preliminary nanoscale spinning experiments were carried out.
【作者单位】： 武汉纺织大学机械工程与自动化学院;湖北数字化纺织装备重点实验室;迪肯大学前沿材料学院;
【基金】：湖北省科技支撑计划对外科技合作类项目(2014BHE010)
【分类号】：TB383.1;TQ340.6
【相似文献】
相关博士学位论文 前8条
1 任勃;镍钴基氧化物纳米纤维的静电纺丝法制备及电化学性能研究[D];哈尔滨工程大学;2014年
2 刘方;纳米颗粒改性环氧树脂及其复合材料力学性能研究[D];哈尔滨工程大学;2014年
3 邵韦;稀土掺杂氟化物多层核壳纳米晶上转换和量子剪裁的研究[D];哈尔滨工业大学;2017年
4 李大龙;介孔磷灰石基纳米药物控制释放体系的构建与生物学评价[D];哈尔滨工业大学;2017年
5 杨桂欣;几种纳米功能材料的合成及成像、肿瘤治疗性能研究[D];哈尔滨工程大学;2015年
6 仲崇娜;核壳结构上转换稀土化合物纳米晶的合成、发光性能及抗肿瘤研究[D];哈尔滨工程大学;2014年
7 平浩梁;纳米氧化钙碳酸化反应性能对甲烷蒸汽重整制氢的强化作用[D];浙江大学;2017年
8 刘洪辰;β淀粉样蛋白聚集的聚合物纳米抑制剂的设计合成和作用[D];天津大学;2016年
相关硕士学位论文 前9条
1 闫贵花;静电纺制备聚丙烯腈/纳米纤维素基多孔碳材料及电学性能研究[D];郑州大学;2017年
2 张路f，
本文编号：2211326
本文链接：https://www.wllwen.com/shekelunwen/minzhuminquanlunwen/2211326.html